The Monolithic Refractory For Blast Furnace |
Technical Data
1.the phosphate mortar for clay brick and high alumina brick
Item |
unit |
index |
NP-45 the phosphate mortar for clay |
LP-70 the phosphate mortar for high alumina |
Refractoriness ≥ |
℃ |
1750 |
1790 |
0.2Mpa refractoriness under load ≥ |
℃ |
1200 |
1320 |
particle size |
>0.5 |
mm |
≤ 1% |
≤ 1% |
<0.076 |
mm |
≥ 50% |
≥ 50% |
Modulus of rupture Mpa |
110℃ dry |
Mpa |
≥ 2 |
≥ 2 |
permanent linear change % |
Mpa |
1200℃×3h ≥ 5.9 |
1400℃×3h ≥ 5.9 |
Al2O3 |
% |
≥ 45 |
70 |
adhesive time |
min |
1-2 |
1-2 |
water required |
% |
25-30 |
25-30 |
2.the high-strength clay castable WNJ-2(for thebottom of blast furnace)
Item |
Refractoriness |
permanent linear change |
Bulk density |
0.2Mpa refractoriness under load |
Cold crush strength |
Al2O3 |
Unit |
℃ |
% |
g/cm3 |
℃ |
Mpa |
% |
Index |
≥1600 |
±1 |
≥2.1 |
≥1350 |
≥40 |
≥42 |
3.the gunning max CMG-BF(for the roof,ascending channel,gravity dust separator of BF)
Item |
Bulk density |
Max service tem. |
Modulus of rupture |
Al2O3 |
SiO2 |
permanent linear change % |
W/m.k |
Unit |
g/cm3 |
℃ |
Mpa |
Mpa |
Mpa |
% |
% |
110℃ |
1000℃ |
1000℃ |
Index |
≥1.9 |
1300 |
≥4 |
≥2.5 |
≥4 |
≥35 |
<50 |
-0.2~0 |
-1~0 |
<0.9 |
4.the fibrecastable(the lining of air-intake pipe)
Item |
Bulk density |
Max service tem. |
Cold crush strength |
Solidification time |
Al2O3 |
Fe2O3 |
W/m.k |
Unit |
g/cm3 |
℃ |
Mpa |
h |
% |
% |
1000℃ |
1200℃ |
Index |
0.65-1.3 |
1280 |
0.7-3.0 |
3-8 |
50-55 |
<1 |
0.22 |
0.29 |
5.the corundum castable(the lining of air-intake pipe)
Item |
permanent linear change % |
Bulk density |
Modulus of rupture |
Al2O3 |
Unit |
1400℃ |
g/cm3 |
(110℃×24h)Mpa |
% |
Index |
±0.5 |
≥3 |
≥25 |
≥90 |
Ambition refractories co., ltd. |
|
|
|
|
|